Technical Data
Full specification
Every published figure for the Goldman range, with the test method it was measured under.
| Item | Specification |
|---|---|
| Base material | Covestro PCU |
| PCU type | A Grade |
| Peel strength | ≥ 75 N/cm |
| Maximum temperature | 120 °C |
| Yellowness index | < 2 |
| Anti-acid resistance | Oxalate — 72 h, pass |
| Self-healing | Heat activation at 75 °C |
| Adhesive | Ashland adhesive |
Per film
What differs between them
Clear PPF
| Item | Specification |
|---|---|
| Gloss | ≥ 110 GU |
| Product thickness | 190 ± 10 µm |
| Coating thickness | 20 ± 5 µm |
| Adhesive thickness | 25 ± 5 µm |
| Tensile strength | > 400 |
| Elongation at break | ≥ 450% |
| Item | Specification |
|---|---|
| Gloss | ≥ 110 GU |
| Product thickness | 210 ± 10 µm |
| Coating thickness | 25 ± 5 µm |
| Adhesive thickness | 30 ± 5 µm |
| Tensile strength | > 400 |
| Elongation at break | ≥ 450% |
| Item | Specification |
|---|---|
| Gloss | ≥ 110 GU |
| Product thickness | 240 ± 10 µm |
| Coating thickness | 25 ± 5 µm |
| Adhesive thickness | 30 ± 5 µm |
| Tensile strength | > 400 |
| Elongation at break | ≥ 450% |
Clear Matte PPF
| Item | Specification |
|---|---|
| Gloss | ≥ 60 GU |
| Product thickness | 190 ± 10 µm |
| Coating thickness | 20 ± 5 µm |
| Adhesive thickness | 25 ± 5 µm |
| Tensile strength | > 400 |
| Elongation at break | ≥ 400% |
| Item | Specification |
|---|---|
| Gloss | ≥ 60 GU |
| Product thickness | 210 ± 10 µm |
| Coating thickness | 25 ± 5 µm |
| Adhesive thickness | 30 ± 5 µm |
| Tensile strength | > 350 |
| Elongation at break | ≥ 400% |
Black Glossy PPF
| Item | Specification |
|---|---|
| Gloss | ≥ 110 GU |
| Product thickness | 190 ± 10 µm |
| Coating thickness | 20 ± 5 µm |
| Adhesive thickness | 25 ± 5 µm |
| Tensile strength | > 400 |
| Elongation at break | ≥ 450% |
| Item | Specification |
|---|---|
| Gloss | ≥ 110 GU |
| Product thickness | 210 ± 10 µm |
| Coating thickness | 25 ± 5 µm |
| Adhesive thickness | 30 ± 5 µm |
| Tensile strength | > 400 |
| Elongation at break | ≥ 450% |
Black Matte PPF
| Item | Specification |
|---|---|
| Gloss | ≥ 60 GU |
| Product thickness | 190 ± 10 µm |
| Coating thickness | 20 ± 5 µm |
| Adhesive thickness | 25 ± 5 µm |
| Tensile strength | > 400 |
| Elongation at break | ≥ 400% |
| Item | Specification |
|---|---|
| Gloss | ≥ 60 GU |
| Product thickness | 210 ± 10 µm |
| Coating thickness | 25 ± 5 µm |
| Adhesive thickness | 30 ± 5 µm |
| Tensile strength | > 350 |
| Elongation at break | ≥ 400% |
Every figure here is transcribed from that film's own technical
data sheet. Sunroof Film and Windshield Film have no sheet published
yet and are not listed.
Appearance
Inspection criteria
Liner bubbles, dust, coated bumps and glue lines: visually invisible. Crystal points between 0.1 and 0.6 mm are permitted. Between 0.7 and 2.9 mm, fewer than ten. At 3.0 mm and above, a maximum of one. Protective film is removed before visual inspection.
Documents
Specification sheets
Product documentation for professional evaluation.
Technical reference
Reference test data for the PCF-series base film, per SGS report SUZMR260200089701 dated 03 March 2026, issued to the film manufacturer.
- Gloss 95.8 GU at 60° (BS EN ISO 2813:2014)
- Coating adhesion 5B, 5B, 5B (ASTM D3359-23)
- Tensile strength 35.4 MPa, elongation 410% (ASTM D638-22)
- No visible change after 24 hours in 5% sulfuric acid (ISO 2812-1:2017)
- No visible change after 384 hours at 80 °C
- Neutral salt spray 24 hours, pass (ISO 9227:2022+A1:2024)
- ΔE*ab 0.33 / 0.40 / 0.21 after 2000 hours UV ageing (ASTM G154-23 Cycle 1)